AG601 Fiberglass Sleeving Coated with Acrylic Resin
Description
AG601 fiberglass sleeving is a Class 155°C electrical insulation,manufactured by impregnating and coating a finely braided fiberglass sleeving with a dielectric film of acrylic resin. AG601 sleeving isrecommended as a universal coated sleeving for all thermal requirements from Class 105°C through Class 155°C.
Features
Superior mechanical and electric properties
High heat resistance (class F,155℃)
Excellent compatibility with polyester,phenolic and epoxy resin.
Excellent resistance to oil, acids and alkalis
Applications
widely used in fractional and integral horsepower
motors on leads and crossovers. Other uses exist in dry and oilfilled
transformers, relays of many types, radio and television circuits,
Available
Breakdown voltage
Grade A 7,000 Volts Min. Avg. 5,000 Volts Min. Indiv.
Grade B 4,000 Volts Min. Avg. 2,500 Volts Min. Indiv.
Grade C-1 2,500 volts Min. Avg. 1,500 Volts Min. Indiv.
Grade C-2 1,500 Volts Min. Avg. 800 Volts Min. Indiv.
Sizes
In continuous spooled lengths or cut lengths in 1000mm per piece
Colors
Black, yellow, white and natural.
Other colours are available on request
Technical Data
|
Inner Diameter Wall Thickness |
|||
|
Size |
Tolerance |
Minimum |
Maximun |
|
1-3 |
±0.20 |
0.20 |
0.60 |
|
4-9 |
±0.30 |
0.30 |
0.70 |
|
10-16 |
±0.50 |
0.50 |
0.80 |
Performance Index (Table 2)
|
Performance |
Index |
|
|
Ⅱ 4000 |
|
Ⅲ 2500 |
|
|
Ⅳ 1000 |
|
|
Bending at low temperature |
No cracking or detachment of the coating shell be visible after 60 min at -15℃ |
|
Bending after heat treatment |
No cracking or detachmant of the coating shell be visible after 48±1hr at 155℃±3℃ |
|
The other performances |
Reference to GB7113-7117-86 |
|
Property |
Requirements |
|||
|
Proof Voltage (not lower than)kv |
under normal conditions |
after dampening |
after winding |
|
|
2.5 kv |
4 kv |
1.2 kv 2kv |
1.5 kv 2.5kv |
|
|
Coating stability |
Temp 20o 5 the sleeving has been wound around the specified mandrel for 1 hour. The coating should not crack or appear detached. |
|||
|
The sleeving is treated for 2hours at a temperature of 10 to 15o C below zero. Then has been wound around the specified mandrel immediately. Coating should not crack ar appear detached. |
||||
|
The sleeving treated at a temperature of 130o 2o C for 24 hours and is wound around a specific mandrel at the room temperature of 20o 2o C The coating should not crack or appear detached. |
||||
|
Oil resistance |
The sleeving dipped in transformer oil for 24 hours at a temperature of 105 2 C. The coating should not crack or appear detached. But the colour of the sleeving is allowed to grow darker. |
|||
|
Benzene resistance |
The sleeving kept in methyl benzene at a normal atmospheric temperature for 4 hours. The coating should not be sticky or show delamination. |
|||