PTFE Coated Glass Fabrics and tapes with Pressure Sensitive Adhesive
Category:
High Temperature & Heat Resistant Application
Keywords:
POWERWELL
DESCRIPTION
Description
Woven glass fabric coated with PTFE (polytetrafluoroethylene) and silicone pressure sensitive adhesive which provides an excellent release surface for a diversity of industrial applications requiring high temperature, electrical resistance, mechanical strength, fire retardancy and cost effectiveness.
Features
These products are produced with either a silicone or acrylic pressure sensitive adhesive system.
The silicone adhesive coated products have a continuous operating temperature range between -70°C and +260°C while the acrylic adhesive coated products provides high initial tack,enhanced solvent resistance and a continuous service temperature range of -40°C to +170°C.Textured PVC yellow liner is applied to the silicone adhesive surface and smooth HDPE blue liner is applied to the acrylic adhesive surface for easy application
Applications
Easy release surface on heat sealing and packaging machines, ironing and pressing equipment, covering drying cylinders, lining chutes, release surface on bonding tools.
Technical Data
Adhesive System |
Standard Width (mm) |
Total Thickness (mm) |
Backing Thickness (mm) |
Backing Weight (g/m²) |
Adhesion . (N/5cm) |
Maximum Temperature (°C) |
Silicone |
1000 |
0,12 |
0,07 |
140 |
22 |
260 |
Silicone |
1000 |
0,17 |
0,12 |
240 |
27 |
260 |
Silicone |
1000 |
0,18 |
0,13 |
270 |
27 |
260 |
Silicone |
1000 |
0,19 |
0,14 |
296 |
28 |
260 |
Silicone |
1000 |
0,20 |
0,15 |
320 |
28 |
260 |
Silicone |
1000 |
0,27 |
0,22 |
455 |
30 |
260 |
Silicone |
1000 |
0,37 |
0,32 |
620 |
31 |
260 |
Acrylic |
1000 |
0,12 |
0,07 |
140 |
26 |
170 |
Acrylic |
1000 |
0,17 |
0,12 |
240 |
30 |
170 |
Acrylic |
1000 |
0,18 |
0,13 |
270 |
30 |
170 |
Acrylic |
1000 |
0,19 |
0,14 |
296 |
31 |
170 |