AG601 Fiberglass Sleeving Coated with Acrylic Resin

Details

Number of views:
1016

AG601 Fiberglass Sleeving Coated with Acrylic Resin

Retail price
0.0
Yuan
Market price
0.0
Yuan
Number of views:
1016
Product serial number
604
Quantity
-
+
Stock:
0
1
Product description

AG601 FIBERGLASS SLEEVING COATED

WITH ACRYLIC RESIN

 

 

Description

AG601 fiberglass sleeving is a Class 155°C electrical insulation,manufactured by impregnating and coating a finely braided fiberglass sleeving with a dielectric film of acrylic resin. AG601 sleeving isrecommended as a universal coated sleeving for all thermal requirements

 

Features

●Superior mechanical and electric properties

●High heat resistance (class F,155)

●Excellent compatibility with polyester,phenolic and epoxy resin.

●excellent resistance to oil, acids and alkalis

 

Applications

widely used in fractional and integral horsepower

motors on leads and crossovers. Other uses exist in dry and oilfilled

transformers, relays of many types, radio and television circuits,
 

 

Available

Breakdown voltage

Grade A 7,000 Volts Min. Avg. 5,000 Volts Min. Indiv.

Grade B 4,000 Volts Min. Avg. 2,500 Volts Min. Indiv.

Grade C-1 2,500 volts Min. Avg. 1,500 Volts Min. Indiv.

Grade C-2 1,500 Volts Min. Avg. 800 Volts Min. Indiv.

 

Sizes

In continuous spooled lengths or cut lengths in 1000mm per piece

 

Colors

Black, yellow, white and natural.

Other colours are available on request

 

 POWERWELL

 

 POWERWELL

 

Technical Data

 

Inner Diameter      WallThickness
Size Tolerance Minimum Maximun
1-3 ±0.20 0.2 0.6
4-9 ±0.30 0.3 0.7
10-16 ±0.50 0.5 0.8

 

Performance Index (Table 2)

 

Performance                            Index
Breakdown Voltage(even) 4000
2500
1000
Bending at low temperature No cracking or detachment of the coating shell be visible after 60 min at -15
Bending after heat treatment No cracking or detachmant of the coating shell be visible after 48±1hr at 155±3
The other performances Reference to GB7113-7117-86

 

Property  Requirements 
Proof Voltage (not lower than)kv under normal conditions  after dampening  after winding 
2.5 kv 4 kv  1.2 kv 2kv  1.5 kv 2.5kv 
Coating stability Temp 20o 5 the sleeving has been wound around the specified mandrel for 1 hour. The coating should not crack or appear detached. 
The sleeving is treated for 2hours at a temperature of 10 to 15o C below zero. Then has been wound around the specified mandrel immediately. Coating should not crack ar appear detached. 
The sleeving treated at a temperature of 130o 2o C for 24 hours and is wound around a specific mandrel at the room temperature of 20o 2o C The coating should not crack or appear detached. 
Oil resistance  The sleeving dipped in transformer oil for 24 hours at a temperature of 105 2 C. The coating should not crack or appear detached. But the colour of the sleeving is allowed to grow darker. 
Benzene resistance  The sleeving kept in methyl benzene at a normal atmospheric temperature for 4 hours. The coating should not be sticky or show delamination. 
Scan the QR code to read on your phone
We could not find any corresponding parameters, please add them to the properties table
puhui

ADD: 158 WU YI ROAD, CHANGSHA, HUNAN, CHINA
TEL:
+86-731-8229 9698, 8224 3908
FAX: +86-731-8224 3598
E-mail: 
market@hnpowerwell.com
License:430100000142665

Laminated Transformer Board
Adhensive Tape transformer
Transformer Plywood
Cotton Banding Tape
Spacing Elements

Flexible Insulation Laminate
Cotton Banding Tape
NHN Nomex Paper/Polyimide Film Composite
Adhensive Tape transformer
Laminated Transformer Board
Electrical Grade Insulating Kraft Paper

Copyright 2012 HUNAN POWERWELL INDUSTRIAL CO., LTD.   湘ICP备12002985号  www.300.cn